Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow | % | ASTM D-955 | 0.40-0.70 |
| Density / Specific Gravity | | g/cm | ASTM D-792 | 1.07 |
| Density / Specific Gravity | | Kg/m | ISO 1183 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strain(Break) | | % | ASTM D-638 | |
| Tensile Strain(Break) | | % | ISO 527-2 | |
| Notched Izod Impact Strength | -30℃，3.18mm | J/m | ASTM D-256 | 139 |
| Notched Izod Impact Strength | 23℃，6.35mm | J/m | ASTM D-256 | 117 |
| Tensile Modulus | | MPa | ISO 527-2 | 2300 |
| Rockwell Hardness | | R-Scale | ASTM D-785 | 108 |
| Flexural Modulus | | MPa | ASTM D-790 | 2350 |
| Flexural Strength | | | ASTM D-790 | 73.8 |
| Charpy Notched Impact Strength | -30℃ | KJ/m | ISO 179/1eA | |
| Charpy Notched Impact Strength | 23℃ | KJ/m | ISO 179/1eA | 15.0 |
| Charpy impact strength | -30℃ | KJ/m | ISO 179/1eU | 35.5 |
| Charpy impact strength | 23℃ | KJ/m | ISO 179/1eU | 68.9 |
| Tensile Strength(Yield) | | MPa | ASTM D-638 | 49.0 |
| Tensile Strength(Yield) | | MPa | ISO 527-2 | 47.0 |
| Tensile Strain(Yield) | | % | ISO 527-2 | 6.0 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame retardancy | 1.59mm | | UL 94 | HB |
| Flame retardancy | 3.18mm | | UL 94 | HB |
| Linear thermal expansion coefficient | Flow | cm/cm/℃ | ISO 11359-2 | 0.000077 |
| Linear thermal expansion coefficient | Transverse | cm/cm/℃ | ISO 11359-2 | 0.000077 |
| Vicat Softening Temperature | | ℃ | ASTM D-1525 | 103 |
| Vicat Softening Temperature | 50℃/h，B(50N) | ℃ | ISO 306 | |
| Deflection Temperature Under Load? | 1.80MPa，未退火 | ℃ | ASTM D-648 | 91.1 |
| Glass Transition Temperature | | ℃ | ISO 11357-2 | |
| Flame Rating | 3.20mm | | ISO 1210 | HB |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 220℃/10kg | g/10min | ASTM D-1238 | 22 |
| Melt index | 220℃/10kg | cm | ISO 1133 | 22.5 |
| Moisture Absorption | | % | ISO 62 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.