Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ASTM D955 | ≤0.5 | % |
| Rockwell Hardness | 23℃ | ASTM D785 | 83 | |
| Melt Mass-Flow Rate | 200℃;5kg荷重 | ASTM D1238 | 2.5 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 23℃,1/8英寸,5mm/min | ASTM D638 | 710 | kg/cm2 |
| 23℃,1/8英寸,5mm/min | ASTM D638 | 700 | kg/cm2 |
| Notched Izod Impact Strength | 23℃,1/4英寸,切割 | ASTM D256 | 1.8 | kg-cm/cm |
| Notched Izod Impact Strength | 23℃,1/8英寸,切割 | ASTM D256 | 1.9 | kg-cm/cm |
| Tensile Strength | 23℃,2.8mm/min | ASTM D790 | 34000 | kg/cm2 |
| Tensile Strength | 23℃,2.8mm/min | ASTM D790 | 1100 | kg/cm2 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame retardancy | 1/16英寸 | UL94 | HB | |
| Deflection Temperature Under Load? | 未退火,1/2英寸,18.56kg/cm²荷重压力 | ASTM D648 | 91 | °C |
| Vicat Softening Temperature | 1/8英寸,1kg荷重 | ASTM D1525 | 104 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.