Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D1505 | 0.941 | g/cm² |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 8.0 | g/10min |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 8.0 | g/10min |
| Vinyl Acetate Content | | | 18.0 | wt% |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | | ASTM D-2240 | 90 | |
| Tensile Modulus | | ASTM D-1708 | 51 | Mpa |
| Tensile Strength | | ASTM D-1708 | 18 | Mpa |
| Tensile Elongation | 断裂 | ASTM D-1708 | 600-900 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting Temperature | DSC | ASTM D-3418 | 86 | °C |
| Vicat Softening Temperature | | ASTM D-1525 | 61 | °C |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 61 | ℃（℉） |
| Vicat Softening Temperature | | ASTMD1525 | 61.0 | °C |
| Vicat Softening Temperature | | ISO306 | 61.0 | °C |
| Melting temperature (DSC) | | ISO3146 | 86.0 | °C |
| Peak Melting Temperature | | ASTMD3418 | 86.0 | °C |
| Vicat Softening Temperature | | ASTM E-28 | 150 | °C |
| Peak Melting Temperature | 石蜡 | | 66 | °C |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | <230 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| VA Content | | | 18 | % |
| Melt index | 190℃/2.16kg | ASTM D-1238 | 8 | g/10min |
| Density | | ASTM D-792 | 0.941 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.