Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.10to0.30 | % |
| Modeling Shrinkage | MD：3.20mm | ISO2577 | 0.10to0.30 | % |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.30 | % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.30 | % |
| Melt Mass-Flow Rate | 315°C/2.16kg | ASTMD1238 | 13 | g/10min |
| Melt Mass-Flow Rate | 315°C/2.16kg | ISO1133 | 13 | g/10min |
| Ash Content | | ISO3451 | 50 | % |
| Density / Specific Gravity | | ASTMD792 | 1.56 | g/cm³ |
| Density / Specific Gravity | | ISO1183 | 1.56 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 屈服 | ASTMD638 | 216 | Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 2.7 | % |
| Flexural Strength | | ASTMD790 | 275 | Mpa |
| Flexural Stress | | ISO178 | 270 | Mpa |
| Flexural Modulus | | ISO178 | 15500 | Mpa |
| Flexural Modulus | | ASTMD790 | 13200 | Mpa |
| Tensile Modulus | | ISO527-2/50 | 12000 | Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 185 | Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 188 | Mpa |
| Tensile Strain | 断裂 | ISO527-2/50 | 3.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 280 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 191 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 16 | kJ/m² |
| 23°C | ISO179/1eA | 16 | kJ/m² |
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 120 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ISO2039-2 | 116 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.