Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.65 | % |
| Modeling Shrinkage | TD2.0mm | ISO294-4 | 0.70 | % |
| Moisture Absorption | (23°C,24hr) | ISO62 | 0.30 | % |
| Moisture Absorption | (23°C,50RH) | ISO62 | 0.12 | % |
| Density / Specific Gravity | | ISO1183 | 1.2 | g/cm³ |
| Melt Mass-Flow Rate | 300℃/1.2Kg | ISO1133 | 19.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Creep Modulus | 1Hr | ISO899-1 | 2200 | Mpa |
| Tensile Creep Modulus | 1000Hr | ISO899-1 | 1900 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 14 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 75 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 12 | kJ/m² |
| Tensile Elongation?(Break) | 23°C | ISO527-2 | >50 | % |
| Tensile Modulus | 23°C | ISO527-2 | 2400 | Mpa |
| Tensile Strength | 23°C | ISO527-2 | 66.0 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2350 | Mpa |
| Flexural Strength | 23°C | ISO178 | 98.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa未退火 | ISO75-2/Bf | 136 | °C |
| Deflection Temperature Under Load? | 1.80MPa退火 | ISO75-2/Af | 124 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 143 | °C |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation strength | | IEC60243-1 | 25 | KV/mm |
| Volume Resistivity | | IEC60093 | 1E+15 | Ω.cm |
| Dissipation Factor? | 23°C | IEC60250 | 5E-04 | 100HZ |
| Dissipation Factor? | 23°C | IEC60250 | 9E-03 | 1MHz |
| Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 250 | V |
| Dielectric Constant | 23°C | IEC60250 | 3.00 | 1MHz |
| Surface resistance | | IEC60093 | 1E+16 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | ISO2039-1 | 116 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Light Transmittance(1000μm) | | ISO13468-2 | 89.0 | % |
| Refractive index of light | | ISO489 | 1.58 | °C |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | 氧指数 | ISO4589-2 | 27 | % |
| Fire rating | | UL-94 | 0.75mm | V-2 |
| Fire rating | | UL-94 | 1.50mm | V-2 |
| Fire rating | | UL-94 | 2.60mm | V-2 |
| Fire rating | | UL-94 | 2.70mm | HB |
| Fire rating | | UL-94 | 3.00mm | HB |
| Fire rating | | UL-94 | 6.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.