Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 200℃，5kg | ISO 1133 | 2.7 | cm3/10min |
| Melt Mass-Flow Rate | 220℃，10kg | ISO 1133 | 30 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 50 mm/min | ISO 527 | 46 | Mpa |
| Flexural Strength | 2mm/min | ISO 178 | 70 | Mpa |
| Flexural Strength | 2 mm/min | ISO 178 | 2.4 | GPa |
| Notched Izod Impact Strength | 4mm/23℃ | ISO 180 | 15 | kJ/m² |
| Charpy Notched Impact Strength | 4mm/23℃ | ISO 179 | 17 | kJ/m3 |
| hardness | | ASTM D785 | 116 | R |
| Tensile Elongation | 50 mm/min | ISO 527 | 20 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8MPa annealed | ISO 75-2 | 100 | °C |
| Heat Deflection Temperature | 1.8MPa unannealed | ISO 75-2 | 85 | °C |
| Vicat Softening Temperature | 10N，50℃/hr | ISO 306 | 105 | °C |
| Flame Rating | 1.5mm | File No.E194560
UL&C-UL | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.