Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 0.85 | g/10min |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 106 | °C |
| Melting temperature (DSC) | | 内部方法 | 123 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness - Tested) | | | 25 | µm |
| Secant Modulus | 1%正割,MD | ASTMD882 | 272 | Mpa |
| Secant Modulus | 2%正割,MD | ASTMD882 | 231 | Mpa |
| Secant Modulus | 1%正割,TD | ASTMD882 | 309 | Mpa |
| Secant Modulus | 2%正割,TD | ASTMD882 | 256 | Mpa |
| Tensile Elongation | MD:断裂 | ASTMD882 | 480 | % |
| Tensile Elongation | TD:断裂 | ASTMD882 | 620 | % |
| Elmendorf Tear Strength | MD | ASTMD1922 | 260 | g |
| Elmendorf Tear Strength | TD | ASTMD1922 | 670 | g |
| Tensile Strength | MD:屈服 | ASTMD882 | 11.9 | Mpa |
| Tensile Strength | TD:屈服 | ASTMD882 | 12.4 | Mpa |
| Tensile Strength | MD:断裂 | ASTMD882 | 43.6 | Mpa |
| Tensile Strength | TD:断裂 | ASTMD882 | 36.0 | Mpa |
| Gardner Impact | | ASTMD1709A | 540 | g |
| Film Puncture Force | | 内部方法 | 28.3 | J/cm³ |
| Film Puncture Energy | | 内部方法 | 5.76 | J |
| Film Puncture Force | | 内部方法 | 64.5 | N |
| Tensile Modulus | MD | ASTMD882 | 98.5 | J/cm³ |
| Tensile Modulus | TD | ASTMD882 | 98.5 | J/cm³ |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | | ASTMD1003 | 20 | % |
| Gloss | 45° | ASTMD2457 | 33 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.