PA612 Zytel® 153HSL-NC010 DUPONT USA
243
- Properties:Mineral reinforcementThermal stability
- Usages:Engineering accessoriesAutomotive Applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.4 | % |
| MD | ISO294-4 | 1.3 | % | |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 3.0 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 1.3 | % | |
| Viscosity number | 96%H2SO4 | ISO307 | 115 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | ISO527-2 | 30 | % | |
| Tensile Stress | 屈服 | ISO527-2 | 62.0 | Mpa |
| Tensile Strain | 屈服 | ISO527-2 | 4.4 | % |
| Tensile Modulus | ISO527-2 | 2400 | Mpa | |
| Flexural Modulus | ISO178 | 2100 | Mpa | |
| Abrasion Resistance | ISO4649 | 6.00 | mm³ |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 135 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 62.0 | °C | |
| Melting Temperature | ISO11357-3 | 218 | °C | |
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| MD：55to160°C | ISO11359-2 | 1.7E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.8E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 7E-08 | m²/s | |
| MD：-- | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50 | 180 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 0.014 | |
| 1MHz | IEC60250 | 0.016 | ||
| Dielectric Strength | IEC60243-1 | 30 | KV/mm | |
| Relative Permittivity | 1MHz | IEC60250 | 3.20 | |
| 100Hz | IEC60250 | 3.60 | ||
| Comparative Tracking Index | IEC60112 | 600 | V | |
| Surface Resistivity | IEC60093 | -- | ohms | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strain (MD) | Yield | ISO527-3 | 4.4 | % |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.9mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 27 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.