PA6 Zytel® 73G15HSL BK363 DUPONT USA
243
- Properties:Thermal stabilityHigh crystallinity
- Usages:Industrial machineryAutomotive components
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.25 |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ThermalConductivityofMelt | 0.20 | W/m/K | ||
| Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
| MD | ISO294-4 | 0.30 | % | |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 7.6 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 2.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | 断裂 | ISO527-2 | 130 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 2.3 | % |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 2.3 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 6500 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 6500 | Mpa | ||
| Tensile Strength | ASTM D638/ISO 527 | 130 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | |
| Izod notch impact strength | ASTM D256/ISO 179 | 40 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting Temperature | ISO11357-3 | 221 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 215 | °C | |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 3.5E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.5E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7.8E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Burning Rate | UL94 | HB | ||
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 204 | ℃（℉） | |
| 0.45MPa,未退火 | ISO75-2/B | 220 | °C | |
| 1.8MPa,未退火 | ISO75-2/A | 204 | °C | |
| Melting Temperature | 221 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 22 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Burning Rate | 1.00mm | ISO3795 | 25 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VDA270 | 4.00 | |||
| VDA277 | 8.50 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.