Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23°C,24hr | ISO62 | 0.70 | % |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 0.70 | % |
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.80 | % |
| MediumDensity | | | 1.10 | g/cm³ |
| Melt Volume flow Rate | 220°C/2.16kg | ISO1133 | 8.80 | cm3/10min |
| Melt Mass-Flow Rate | 220°C/2.16kg | ISO1133 | 8.5 | g/10min |
| Density / Specific Gravity | | ISO1183 | 1.11 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2 | 800 | % |
| Tensile Modulus | | ISO527-2 | 45.0 | Mpa |
| Flexural Modulus | | ISO178 | 45.0 | Mpa |
| Tensile Stress | 10%应变 | ISO527-2 | 3.20 | Mpa |
| Tensile Stress | 50%应变 | ISO527-2 | 6.70 | Mpa |
| Tensile Stress | 断裂 | ISO527-2 | 29.0 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | >300 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Brittleness Temperature | | ISO974 | -96.0 | °C |
| Glass Transition Temperature | | ISO11357-2 | -50.0 | °C |
| Linear thermal expansion coefficient | TD：-40to23°C | ISO11359-2 | 2.8E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：-- | ISO11359-2 | 2E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 2.8E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 2.2E-04 | cm/cm/°C |
| Melting Temperature | | ISO11357-3 | 193 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | IEC60243-1 | 18 | KV/mm |
| Relative Permittivity | 100Hz | IEC60250 | 4.80 | |
| Relative Permittivity | 1MHz | IEC60250 | 4.70 | |
| Comparative Tracking Index | | IEC60112 | 600 | V |
| Dissipation Factor? | 100Hz | IEC60250 | 0.013 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 | |
| Surface Resistivity | | IEC60093 | 3E+14 | ohms |
| Volume Resistivity | | IEC60093 | 4E+12 | ohms·cm |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tearing Strength | 横向流量 | ISO34-1 | 100 | kN/m |
| Tearing Strength | 流量 | ISO34-1 | 100 | kN/m |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| WaterVaporTransmissionRate | 23°C,85%RH,25µm | DIS15106-1/-2 | 900 | g/m²/24hr |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | NoBreak | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | NoBreak | |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | NoBreak | |
| Notched Izod Impact Strength | -40°C | ISO180/1A | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | NoBreak | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D | ISO868 | 37 | |
| Shore Hardness | 邵氏D,15秒 | ISO868 | 33 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Oxygen Index | | ISO4589-2 | 20 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 10.0 | µgC/g |
| Odor | | VDA270 | 4.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.