Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.08 | kg·cm/cm(J/M)ft·lb/in |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 30 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ASTMD955 | 0.40到0.60 | % |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 30 | g/10min |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 31.4 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO178 | 3700 | Mpa |
| Flexural Stress | | ISO178 | 123 | Mpa |
| Tensile Stress | 屈服 | ISO527-2/5 | 64.1 | Mpa |
| Flexural Modulus | | ASTM D790/ISO 178 | 3330(MPa) | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 97(MPa) | kg/cm²(MPa)[Lb/in²] |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | HB | |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 90 | ℃（℉） |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 86.8 | °C |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 109 | ℃（℉） |
| Vicat Softening Temperature | | ISO306/B | 102 | °C |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| RTI | | UL746 | 50.0 | °C |
| Ball PressureTest | | EMAC | 95 | °C |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.