Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | 内部方法 | 0.4-0.7 | % |
| Melt Mass-Flow Rate | 200°C/5.0 kg | ASTM D-1238 | 2.2 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D-1238 | 22 | g/10min |
| Density / Specific Gravity | | ASTM D-792 | 1.05 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 23℃ | ASTM D-638 | 46 | Mpa |
| Unnotched Izod Impact Strength | 23℃,6.35mm | ASTM D-256 | 220 | J/m |
| Rockwell Hardness | R级,23℃ | ASTM D-785 | 108 | |
| Flexural Modulus | 23℃ | ASTM D-790 | 2650 | Mpa |
| Flexural Strength | 23℃ | ASTM D-790 | 78 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,退火,12.7mm | ASTM D-648 | 85 | °C |
| Deflection Temperature Under Load? | 1.8MPa,退火 | ASTM D-648 | 95 | °C |
| UL flame retardant rating | 1.50 mm, All Colors | UL 94 | HB | |
| Vicat Softening Temperature | | ASTM D-1525 | 99 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.