Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD1 | 内部方法 | 0.40到0.60 | % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.60 | % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 80.0 | Mpa |
| Tensile Modulus | | ISO527-2/1 | 2500 | Mpa |
| Flexural Modulus | | ISO178 | 2400 | Mpa |
| yield | | ISO527-2/5 | 55.0 | Mpa |
| yield | | ISO527-2/50 | 59.0 | Mpa |
| yield | | ISO527-2/5,ISO527-2/50 | 4.0 | % |
| fracture | | ISO527-2/5 | 120 | % |
| fracture | | ISO527-2/50 | >50 | % |
| fracture | | ISO527-2/5 | 55.0 | Mpa |
| fracture | | ISO527-2/50 | 59.0 | Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 125 | mg |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD：23到60°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
| Ball PressureTest | 105°C7 | IEC60695-10-2 | Pass | |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| Thermal Conductivity | | ISO8302 | 0.20 | W/m/K |
| RTI | | UL746 | 50.0 | °C |
| | ISO306/B50 | 119 | °C |
| | ISO306/B120 | 120 | °C |
| 0.45MPa, Unannealed,100mm Span | | ISO75-2/Be | 125 | °C |
| 1.8MPa, Unannealed,100mm Span | | ISO75-2/Ae | 101 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 1MHz | IEC60250 | 0.015 | |
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 | KV/mm |
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Relative Permittivity | 1MHz | IEC60250 | 2.90 | |
| Comparative Tracking Index | | IEC60112 | 175 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 45 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R计秤 | ISO2039-2 | 118 | |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 104 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.750mm | UL94 | HB | |
| UL flame retardant rating | 3.00mm | UL94 | HB | |
| Glow Wire Flammability Index | 3.20mm | IEC60695-2-12 | 750 | °C |
| Oxygen Index | | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.