ASA/PC GELOY™ HRA170-BR6A1436 SABIC INNOVATIVE US
422
- Properties:Weather resistanceheat-resistingHigh impact resistance
- Usages:Automotive sector
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.60 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Melt Volume flow Rate | 260°C/5.0 kg | ISO 1133 | 17.0 | cm3/10min |
| Modeling Shrinkage - Flow | 内部方法 | 0.40 到 0.60 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO 178 | 85.0 | Mpa | |
| Tensile Modulus | ISO 527-2/1 | 2500 | Mpa | |
| Tensile Stress | 屈服 | ISO 527-2/5 | 55.0 | Mpa |
| 屈服 | ISO 527-2/50 | 62.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 60.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 62.0 | Mpa | |
| Tensile Strain | 屈服 | ISO 527-2/5 | 5.0 | % |
| 屈服 | ISO 527-2/50 | 4.0 | % | |
| 断裂 | ISO 527-2/5 | 130 | % | |
| 断裂 | ISO 527-2/50 | > 50 | % | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 95.0 | mg |
| Flexural Modulus | ISO 178 | 2400 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 121 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 112 | °C | |
| Thermal Conductivity | ISO 8302 | 0.20 | W/m/K | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 129 | °C |
| -- | ISO 306/B120 | 132 | °C | |
| Coefficient of Linear Thermal Expansion (Flow) | 23 到 60°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.013 | |
| Dielectric Strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 | KV/mm |
| Relative Permittivity | 1 MHz | IEC 60250 | 2.80 | |
| Comparative Tracking Index | IEC 60112 | 225 | V |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 100 到 110 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 260 到 290 | °C | ||
| Mold Temperature | 60 到 90 | °C | ||
| Drying Time | 2.0 到 4.0 | hr | ||
| Rear Temperature | 230 到 260 | °C | ||
| Middle Temperature | 250 到 290 | °C | ||
| Front Temperature | 250 到 290 | °C | ||
| Nozzle Temperature | 240 到 280 | °C | ||
| Hopper Temperature | 60 到 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 | kJ/m² |
| 23°C | ISO 179/1eA | 60 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO 180/1A | 15 | kJ/m² |
| 23°C | ISO 180/1A | 45 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R 计秤 | ISO 2039-2 | 120 | |
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 106 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | 3.2 mm | IEC 60695-2-12 | 750 | °C |
| Oxygen Index | ISO 4589-2 | 22 | % | |
| Flame Rating | 1.6 mm, Testing by SABIC | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.