Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ASTMD955 | 0.40到0.70 | % |
| Modeling Shrinkage | -- | ISO294-4 | 0.40到0.70 | % |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 17 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 24 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 断裂 | ASTMD638 | 22 | % |
| Tensile Elongation | 断裂 | ISO527-2/50 | 25 | % |
| Flexural Modulus | -- | ASTMD790 | 2200 | Mpa |
| Flexural Modulus | --2 | ISO178 | 2300 | Mpa |
| Flexural Strength | -- | ASTMD790 | 72.0 | Mpa |
| Flexural Strength | --2 | ISO178 | 65.0 | Mpa |
| Tensile Strength | -- | ASTMD638 | 52.0 | Mpa |
| Tensile Strength | -- | ISO527-2/50 | 47.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | -- | ASTMD15256 | 95.0 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 96.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ASTMD648 | 85.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火5 | ISO75-2/A | 78.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 7.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 15 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 60 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.