Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1690 | |
| Modeling Shrinkage | | ASTM D955 | 0.85 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.14 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 0.62 | % |
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.14 | % |
| Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.20 | % |
| Ejection Temperature | | | 170 | °C |
| Melt Volume flow Rate | 280°C/2.16kg | ISO1133 | 2.50 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | 15600 | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 13300 | Mpa |
| Tensile Stress | 断裂 | ISO527-2 | 182 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 2.0 | % |
| Tensile Modulus | | ASTM D412/ISO 527 | 15500 | kg/cm²(MPa)[Lb/in²] |
| Tensile Modulus | | ISO527-2 | 15500 | Mpa |
| Rockwell Hardness | | ASTM D785 | 100 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 13500 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ISO178 | 13500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | HB | |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 250 | ℃（℉） |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 226 | ℃（℉） |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 226 | °C |
| Deflection Temperature Under Load? | 8.0MPa,未退火 | ISO75-2/C | 180 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 8.3E-05 | cm/cm/°C |
| Vicat Softening Temperature | | ISO306/B50 | 230 | °C |
| Melting Temperature | | ISO11357-3 | 252 | °C |
| Thermal Conductivity | | | 0.32 | W/m/K |
| Effective Thermal Diffusivity | | | 1.4E-07 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Dielectric Strength | | IEC60243-1 | 32 | KV/mm |
| Relative Permittivity | 100Hz | IEC60250 | 4.50 | |
| Relative Permittivity | 1MHz | IEC60250 | 4.40 | |
| Comparative Tracking Index | | IEC60112 | 250 | V |
| Dissipation Factor? | 100Hz | IEC60250 | 7E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.011 | |
| Surface Resistivity | | ASTM D257/IEC 60093 | 1.00E+14 | Ω |
| Surface Resistivity | | IEC60093 | 1E+14 | ohms |
| Dielectric Constant | | ASTM D150/IEC 60250 | 4.5 | |
| Dielectric Constant | | ASTM D150/IEC 60250 | 4.4 | |
| Volume Resistivity | | ASTM D257/IEC 60093 | 1.00E+13 | Ω.cm |
| Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M计秤 | ISO2039-2 | 100 | |
| Rockwell Hardness | R计秤 | ISO2039-2 | 120 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| Oxygen Index | | ISO4589-2 | 20 | % |
| FMVSS Flammability | | FMVSS302 | B | |
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.