Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 260℃/2.16kg | IOS 1133 | 22 | cm3/10min |
| hardness | 1/2''（HRR） | ASTM D785 | 118 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 3.2mm,4mm/23℃ | IOS 179 | 46 | kJ/m² |
| Tensile Strength | 50mm/min | IOS 527 | 60 | Mpa |
| Tensile Elongation | 50mm/min | IOS 527 | 120 | % |
| Flexural Modulus | 2mm/min | IOS 178 | 2.5 | GPa |
| Flexural Strength | 2mm/min | IOS 178 | 90 | Mpa |
| Izod Impact Strength | 3.2mm,4mm/23℃ | IOS 180 | 45 | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa 未退火 | IOS 75-2 | 82 | °C |
| Deflection Temperature Under Load? | 0.46MPa 未退火 | IOS 75-2 | 91 | °C |
| Vicat Softening Temperature | 10N，50℃/hr | IOS 306 | 107 | °C |
| Vicat Softening Temperature | 50N，50℃/hr | IOS 306 | 105 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.