Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-756S TAIWAN CHIMEI
POLYLAC®
Household goods
High mobility
UL
MSDS
RoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-756S
Density / Specific Gravity
--3
ASTMD792
g/cm³
1
Density / Specific Gravity
23°C
ISO1183
g/cm³
1
Melt Volume flow Rate
220°C/10.0kg
ISO1133
cm3/10min
6
Melt Mass-Flow Rate
200°C/5.0kg
ASTMD1238
g/10min
6
Modeling Shrinkage
ISO294-4
%
0
Mechanical Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-756S
Tensile Strength
屈服4
ASTMD638
Mpa
3
Tensile Strength
屈服
ISO527-2/50
Mpa
4
Tensile Strength
断裂
ISO527-2/50
Mpa
3
Tensile Elongation
断裂4
ASTMD638
%
3
Tensile Elongation
断裂
ISO527-2/50
%
3
Flexural Modulus
--5
ASTMD790
Mpa
2
Flexural Modulus
--6
ISO178
Mpa
2
Flexural Strength
--5
ASTMD790
Mpa
5
Flexural Strength
--6
ISO178
Mpa
6
Thermal Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-756S
Deflection Temperature Under Load?
1.8MPa,未退火
ASTMD648
°C
8
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/A
°C
8
Deflection Temperature Under Load?
1.8MPa,退火
ASTMD648
°C
9
Deflection Temperature Under Load?
1.8MPa,退火
ISO75-2/A
°C
9
Vicat Softening Temperature
--
ASTMD15257
°C
1
Vicat Softening Temperature
--
ISO306/A50
°C
1
Vicat Softening Temperature
--
ISO306/B50
°C
9
Linear thermal expansion coefficient
MD
ISO11359-2
cm/cm/°C
8
Impact Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-756S
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
8
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
1
Notched Izod Impact Strength
23°C,3.20mm
ASTMD256
J/m
2
Notched Izod Impact Strength
23°C,6.40mm
ASTMD256
J/m
1
Notched Izod Impact Strength
-30°C
ISO180/1A
kJ/m²
7
Notched Izod Impact Strength
23°C
ISO180/1A
kJ/m²
1