Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-747H TAIWAN CHIMEI
POLYLAC®
Refrigerator、Electrical field、Electronic field、Electrical appliances
Chemical resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747H
Apparent Density
ISO60
g/cm³
1
Density
ASTMD792
g/cm³
1
Melt Mass-Flow Rate
200°C/5.0kg
ASTMD1238
g/10min
0
Melt Mass-Flow Rate
220°C/10.0kg
ASTMD1238
g/10min
2
Melt Mass-Flow Rate
220°C/10.0kg
ISO1133
g/10min
3
Modeling Shrinkage
ISO294-4
%
0
Mechanical Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747H
Tensile Stress
屈服
ISO527-2/50
Mpa
4
Tensile Stress
断裂
ISO527-2/50
Mpa
3
Tensile Stress
3.00mm3
ASTMD638
Mpa
4
Tensile Elongation
断裂,3.00mm3
ASTMD638
%
5
Tensile Elongation
断裂
ISO527-2/50
%
2
Flexural Modulus
6.00mm4
ASTMD790
Mpa
2
Flexural Modulus
--5
ISO178
Mpa
1
Flexural Strength
6.00mm4
ASTMD790
Mpa
6
Flexural Strength
--5
ISO178
Mpa
6
Thermal Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747H
Deflection Temperature Under Load?
1.8MPa,未退火
ASTMD648
°C
8
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/A
°C
8
Deflection Temperature Under Load?
1.8MPa,退火
ASTMD648
°C
9
Deflection Temperature Under Load?
1.8MPa,退火
ISO75-2/A
°C
1
Vicat Softening Temperature
--
ASTMD15256,ISO306/A506
°C
1
Vicat Softening Temperature
--
ISO306/B50
°C
1
Linear thermal expansion coefficient
MD
ISO11359-2
cm/cm/°C
8
Impact Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747H
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
2
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
3
Notched Izod Impact Strength
23°C,3.00mm
ASTMD256
J/m
4
Notched Izod Impact Strength
23°C,6.00mm
ASTMD256
J/m
3
Notched Izod Impact Strength
-30°C
ISO180/1A
kJ/m²
2
Notched Izod Impact Strength
23°C
ISO180/1A
kJ/m²
3