Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EAA 1321 STYRON US
PRIMACOR™
Multi layer composite mat、Food packaging、Food service sector、Food containers
Heat sealing performance、Resistance to stress crac、high strength、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
EAA/STYRON US/1321
monomer Content
内部方法
%
6
Density / Specific Gravity
ASTMD792,ISO1183/A
g/cm³
0
Density / Specific Gravity
g/cm³
0.935
A
Density / Specific Gravity
g/cm³
0.935
I
Melt Mass-Flow Rate
190°C/2.16kg
ASTMD1238,ISO1133
g/10min
2
Mechanical Properties
Test Condition
Test Method
Unit
EAA/STYRON US/1321
Elmendorf Tear Strength (MD)
50.8um
g
270
A
Elmendorf Tear Strength (MD)
50.8um
N
1200
I
Elmendorf Tear Strength (TD)
50.8um
N
1700
I
Elmendorf Tear Strength (TD)
50.8um
g
390
A
Film Thickness (Tested)
um
50.8
Tensile Strength
断裂,模压成型
ISO527-2/508
Mpa
2
Tensile Strength
断裂,模压成型4
ASTMD638
Mpa
2
Tensile Strength
屈服,模压成型
ISO527-2/508
Mpa
1
Tensile Strength
屈服,模压成型4
ASTMD638
Mpa
1
Tensile Strength(Break)
Compression Molded
MPa
20.1
I
Tensile Strength(Break)
Compression Molded
MPa
20.1
A
Tensile Strength (Break TD)
50.8um
MPa
31.8
I
Tensile Strength (Break TD)
50.8um
MPa
31.8
A
Tensile Strength (Break TD)
50.8um
MPa
31.8
I
Tensile Elongation (Break TD)
50.8um
%
510
I
Tensile Elongation (Break TD)
50.8um
%
510
A
Tensile Strength (Yield MD)
50.8um
MPa
11.3
A
Tensile Strength (Yield MD)
50.8um
MPa
11.3
I
Tensile Strength (Yield TD)
50.8um
MPa
11.5
I
Tensile Strength (Yield TD)
50.8um
MPa
11.1
A
Gardner Impact
50.8um
g
410
A
Gardner Impact
50.8um
g
410
I
Tensile Elongation
断裂,模压成型
ISO527-2/508
%
6
Tensile Elongation
断裂,模压成型4
ASTMD638
%
6
Thermal Properties
Test Condition
Test Method
Unit
EAA/STYRON US/1321
Melting temperature (DSC)
内部方法
°C
1
Melting temperature
℃
103
D
Vicat Softening Temperature
℃
88.9
A
Vicat Softening Temperature
℃
88.9
I
Vicat Softening Temperature
ASTMD1525,ISO306
°C
8
Film
Test Condition
Test Method
Unit
EAA/STYRON US/1321
Elmendorf Tear Strength
TD:51µm
ASTMD1922
g
3
Elmendorf Tear Strength
MD:51µm
ISO6383-2
N
1
Elmendorf Tear Strength
TD:51µm
ISO6383-2
N
1
Elmendorf Tear Strength
MD:51µm
ASTMD1922
g
2
Tensile Strength
MD:屈服,51µm
ASTMD882
Mpa
1
Tensile Strength
TD:屈服,51µm
ASTMD882
Mpa
1
Tensile Strength
MD:屈服,51µm
ISO527-3
Mpa
1
Tensile Strength
TD:屈服,51µm
ISO527-3
Mpa
1
Tensile Strength
MD:断裂,51µm
ASTMD882,ISO527-3
Mpa
3
Tensile Strength
TD:断裂,51µm
ASTMD882,ISO527-3
Mpa
3
Gardner Impact
51µm
ASTMD1709B,ISO7765-1/B
g
4
Tensile Elongation
MD:断裂,51µm
ASTMD882,ISO527-3
%
4
Tensile Elongation
TD:断裂,51µm
ASTMD882,ISO527-3
%
5
Processing
Test Condition
Test Method
Unit
EAA/STYRON US/1321
Melt Temperature
℃
193
optical performance
Test Condition
Test Method
Unit
EAA/STYRON US/1321
Haze
50.8µm
ISO14782
%
3
Haze
50.8µm
ASTMD1003
%
3
Haze
50.8um
%
3.7
A
Haze
50.8um
%
3.7
I
Physical
Test Condition
Test Method
Unit
EAA/STYRON US/1321
Melt Mass-Flow Rate
190℃/2.16kg
g/10min
2.6
A
Melt Mass-Flow Rate
190℃/2.16kg
g/10min
2.6
I