Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA612 158 NC010 DUPONT USA
Zytel®
Engineering accessories、Automotive Applications
Mineral reinforcement、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Modeling Shrinkage
ASTM D955
%
1
Moisture Absorption 23℃/24H
ASTM D570/ISO 62
%
1
Physical Properties
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Modeling Shrinkage
TD
ISO294-4
%
1
Modeling Shrinkage
MD
ISO294-4
%
1
Moisture Absorption
饱和,23°C,2.00mm
ISO62
%
3
Moisture Absorption
平衡,23°C,2.00mm,50%RH
ISO62
%
1
Viscosity number
96%H2SO4
ISO307
cm³/g
1
Mechanical Properties
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Nominal Tensile Strain at Break
ISO527-2
%
3
Tensile Elongation?(Break)
ASTM D412/ISO 527
%
3
Tensile Modulus
ASTM D412/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile Modulus
ISO527-2
Mpa
2
Tensile Strength
ASTM D412/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Tensile Strain
屈服
ISO527-2
%
4
Tensile Stress
屈服
ISO527-2
Mpa
6
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
N
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
Thermal Properties
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Glass Transition Temperature
ISO11357-2
°C
6
Deflection Temperature Under Load?
ASTM D648/ISO 75
℃（℉）
1
Deflection Temperature Under Load?
ASTM D648/ISO 75
℃（℉）
6
Deflection Temperature Under Load?
0.45MPa,未退火
ISO75-2/B
°C
1
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/A
°C
6
Melting Temperature
ISO11357-3
°C
2
Vicat Softening Temperature
ISO306/B50
°C
1
Linear thermal expansion coefficient
MD
ISO11359-2
cm/cm/°C
1
Linear thermal expansion coefficient
TD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Dielectric Strength
IEC60243-1
KV/mm
3
Volume Resistivity
IEC60093
ohms·cm
>
Film
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Tensile Strain (MD)
Yield
ISO527-3
%
4
Flammability
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Oxygen Index
ISO4589-2
%
2
Burning Rate
1.00mm
ISO3795
mm/min
<