HIPS HIPS-514 SECCO SHANGHAI
--
Electrical field、Electronic field、Toy
heat-resisting、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
HIPS/SECCO SHANGHAI/HIPS-514
Melt Mass-Flow Rate
ASTM D1238/ISO 1133
g/10min
1
Mechanical Properties
Test Condition
Test Method
Unit
HIPS/SECCO SHANGHAI/HIPS-514
Tensile Elongation?(Break)
ASTM D638/ISO 527
%
5
Tensile Strength(Yield)
ISO 527-2/1993
Mpa
2
Flexural Strength
2mm/min
ISO 178/1993
Mpa
2
Tensile Strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile Elongation
50mm/min
ISO 527-2/1993
%
5
Notched Izod Impact Strength
ISO 180/1993
J/m
7
Notched Izod Impact Strength
ISO 180/1993
J/m
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
7
Thermal Properties
Test Condition
Test Method
Unit
HIPS/SECCO SHANGHAI/HIPS-514
Deflection Temperature Under Load?
ASTM D648/ISO 75
℃（℉）
7
Deflection Temperature Under Load?
1.82MPa
ISO 75-2/1993
°C
7
Vicat Softening Temperature
B50/oil
ISO 306/1994
°C
8
Vicat Softening Temperature
ASTM D1525/ISO R306
℃（℉）
8
Physical
Test Condition
Test Method
Unit
HIPS/SECCO SHANGHAI/HIPS-514
Density
ISO 1183/1987
kg/m
1
Melt index
200℃/5Kg
ISO 1133/1997
g/10min
1