Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 9506F-04 CELANESE USA
TOPAS®
film、Industrial Supplies、auto parts
Low water absorption、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
COC/CELANESE USA/9506F-04
Melt Volume flow Rate
190°C/2.16kg
ISO1133
cm3/10min
1
Melt Volume flow Rate
230°C/2.16kg
ISO1133
cm3/10min
6
Moisture Absorption
饱和,23°C
ISO62
%
0
Mechanical Properties
Test Condition
Test Method
Unit
COC/CELANESE USA/9506F-04
Tensile Modulus
ISO527-2/1A/1000
Mpa
2
Thermal Properties
Test Condition
Test Method
Unit
COC/CELANESE USA/9506F-04
Glass Transition Temperature
ISO11357-2
°C
6
Film
Test Condition
Test Method
Unit
COC/CELANESE USA/9506F-04
38°C
ISO15106-3
g·100µm/(m²·day
0
Elmendorf Tear Strength
MD
ISO6383-2
N
2
Elmendorf Tear Strength
TD
ISO6383-2
N
2
Tensile Modulus
MD
ISO527-3
Mpa
1
Tensile Modulus
TD
ISO527-3
Mpa
2
Tensile Stress
MD:断裂
ISO527-3
Mpa
5
Tensile Stress
TD:断裂
ISO527-3
Mpa
5
Gardner Impact
ISO7765-1
g
<
Tensile Elongation
MD:断裂
ISO527-3
%
2
Tensile Elongation
TD:断裂
ISO527-3
%
3
Oxygen Transmission Rate
23°C,50%RH
ASTMD3985
cm³·mm/m²/atm/24hr
1
optical performance
Test Condition
Test Method
Unit
COC/CELANESE USA/9506F-04
Haze
ISO14782
%
<