Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AS(SAN) 783 ASAHI JAPAN
Stylac™
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
AS(SAN)/ASAHI JAPAN/783
Density
ASTM D792/ISO 1183
kg·cm/cm(J/M)ft·lb/in
1
Melt Mass-Flow Rate
ASTM D1238/ISO 1133
g/10min
9
Physical Properties
Test Condition
Test Method
Unit
AS(SAN)/ASAHI JAPAN/783
Melt Volume flow Rate
220°C/10.0kg
ISO1133
cm3/10min
9
Melt Mass-Flow Rate
220°C/10.0kg
ISO1133
g/10min
9
Modeling Shrinkage
MD
ASTMD955
%
0
Mechanical Properties
Test Condition
Test Method
Unit
AS(SAN)/ASAHI JAPAN/783
Tensile Elongation?(Break)
ASTM D638/ISO 527
%
2
Tensile Strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
7
Tensile Stress
屈服
ISO527-2/5
Mpa
7
Flexural Modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
3
Flexural Modulus
ISO178
Mpa
3
Flexural Strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Flexural Stress
ISO178
Mpa
1
Izod notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Thermal Properties
Test Condition
Test Method
Unit
AS(SAN)/ASAHI JAPAN/783
Ball PressureTest
EMAC
°C
9
RTI
UL746
°C
5
RTIElec
UL746
°C
5
Evolution Calendar intelligent importer
UL746
°C
5
Deflection Temperature Under Load?
ASTM D648/ISO 75
℃（℉）
9
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/A
°C
8
Vicat Softening Temperature
ASTM D1525/ISO R306
℃（℉）
1
Vicat Softening Temperature
ISO306/B
°C
1