MABS TR557 NP LG CHEM KOREA
--
electronic product、Electronic appliances
Transparency level、High impact
UL
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557 NP
Melt Mass-Flow Rate
220°C/10.0 kg
ASTM D1238
g/10 min
2
Modeling Shrinkage - Flow
23°C, 3.20 mm, 注塑
ASTM D955
%
0
Mechanical Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557 NP
Tensile Strength
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
Mpa
4
Tensile Modulus
23°C, 3.20 mm, 注塑
ASTM D638
Mpa
2
Tensile Elongation
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
%
>
Tensile Elongation
断裂, 23°C, 3.20 mm, 注塑
ASTM D638
%
1
Flexural Modulus
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
2
Flexural Strength
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
7
Thermal Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557 NP
RTI
UL 746
°C
5
RTI Elec
UL 746
°C
5
RTI Imp
UL 746
°C
5
Vicat Softening Temperature
ASTM D15257
°C
8
Deflection Temperature Under Load?
1.8 MPa, 未退火, 6.40 mm, 注塑
ASTM D648
°C
8
Injection
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557 NP
Back Pressure
Mpa
2
Drying Time
hr
2
Drying Temperature
°C
8
Processing (Melt) Temp
°C
1
Rear Temperature
°C
1
Front Temperature
°C
2
Middle Temperature
°C
1
Screw Speed
rpm
3
Mold Temperature
°C
4
Nozzle Temperature
°C
1
optical performance
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557 NP
Transmittance
3200 µm, 注塑
ASTM D1003
%
9
Haze
注塑
ASTM D1003
%
2