Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 73G30HSL DUPONT USA
Zytel®
Electronic and electrical、Automotive Applications
Thermal stability、30% filler by weight、Filler: Glass fiber reinf
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
Density / Specific Gravity
ISO1183
g/cm³
1
Melt Volume flow Rate
250°C/5.0kg
ISO1133
cm3/10min
1
Modeling Shrinkage
TD
ISO294-4
%
0
Modeling Shrinkage
MD
ISO294-4
%
0
Moisture Absorption
饱和,23°C,2.00mm
ISO62
%
6
Moisture Absorption
平衡,23°C,2.00mm,50%RH
ISO62
%
1
Mechanical Properties
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
Tensile Creep Modulus
1hr
ISO899-1
Mpa
-
Tensile Modulus
ISO527-2
Mpa
9
Tensile Creep Modulus
1000hr
ISO899-1
Mpa
-
Tensile Strain
断裂
ISO527-2
%
3
Tensile Stress
断裂
ISO527-2
Mpa
1
Flexural Modulus
ISO178
Mpa
8
Flexural Stress
ISO178
Mpa
2
Thermal Properties
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
Glass Transition Temperature
ISO11357-2
°C
6
Deflection Temperature Under Load?
0.45MPa,未退火
ISO75-2/B
°C
2
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/A
°C
2
Melting Temperature
ISO11357-3
°C
2
Vicat Softening Temperature
ISO306/B50
°C
2
Linear thermal expansion coefficient
MD
ISO11359-2
cm/cm/°C
2
Linear thermal expansion coefficient
TD
ISO11359-2
cm/cm/°C
7
Impact Properties
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
Multi-Axial Instrumented Impact Energy
23°C
ISO6603-2
J
3
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Charpy Unnotched Impact Strength
-30°C
ISO179/1eU
kJ/m²
8
Charpy Unnotched Impact Strength
23°C
ISO179/1eU
kJ/m²
1
Notched Izod impact strength
23°C
ISO180/1U
kJ/m²
8
Notched Izod Impact Strength
-30°C
ISO180/1A
kJ/m²
1
Notched Izod Impact Strength
23°C
ISO180/1A
kJ/m²
1
hardness
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
Ball Indentation Hardness
H961/30
ISO2039-1
Mpa
2
Flammability
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
Oxygen Index
ISO4589-2
%
2
Burning Rate
1.00mm
ISO3795
mm/min
5
atomization
F-value(refraction)
ISO6452
%
9
atomization
G-value(condensate)
ISO6452
g
1
Supplementary information
Test Condition
Test Method
Unit
PA66/DUPONT USA/73G30HSL
EmissionofOrganicCompounds
VDA277
µgC/g
8