Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EVOH F101B NIPPON GOHSEI
--
--
copolymer、Lubricity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
内部方法
mol%
3
Melt Mass-Flow Rate
190°C/2.16kg
ISO1133
g/10min
1
Melt Mass-Flow Rate
210°C/2.16kg
ISO1133
g/10min
3
Mechanical Properties
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Tensile Modulus
ISO527-2
Mpa
2
Tensile Strain
断裂
ISO527-2
%
1
Tensile Stress
断裂
ISO527-2
Mpa
3
Flexural Modulus
ISO178
Mpa
3
Thermal Properties
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Glass Transition Temperature
ISO11357-2
°C
6
Peak Crystallization Temperature?
ISO11357-3
°C
1
Melting temperature
ISO11357-3
°C
1
Vicat Softening Temperature
ISO306
°C
1
Film
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Water Vapor Transmission Rate
ASTME96
g·mm/m²/atm/24hr
1
Oxygen Transmission Rate
20°C,100%RH
ISO14663-2
cm³·mm/m²/atm/24hr
0
Oxygen Transmission Rate
20°C,35%RH
ISO14663-2
cm³·mm/m²/atm/24hr
6
Oxygen Transmission Rate
20°C,65%RH
ISO14663-2
cm³·mm/m²/atm/24hr
8
Oxygen Transmission Rate
20°C,85%RH
ISO14663-2
cm³·mm/m²/atm/24hr
0
Oxygen Transmission Rate
20°C,90%RH
ISO14663-2
cm³·mm/m²/atm/24hr
0
Oxygen Transmission Rate
20°C,0%RH
ISO14663-2
cm³·mm/m²/atm/24hr
4
Impact Properties
Test Condition
Test Method
Unit
EVOH/NIPPON GOHSEI/F101B
Notched Izod impact strength
ISO180
kJ/m²
2