Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EAA 3330 STYRON US
PRIMACOR™
Food service sector
Heat sealing performance、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
EAA/STYRON US/3330
monomer Content
内部方法
%
6
Melt Mass-Flow Rate
190°C/2.16kg
ASTMD1238,ISO1133
g/10min
5
Mechanical Properties
Test Condition
Test Method
Unit
EAA/STYRON US/3330
Tensile Strength
屈服,模压成型
ASTMD638,ISO527-2
Mpa
8
Tensile Strength
断裂,模压成型
ASTMD638,ISO527-2
Mpa
1
Tensile Strength(Break)
Compression Molded
MPa
17.4
A
Tensile Strength(Break)
Compression Molded
MPa
17.4
I
Tensile Elongation?(Break)
Compression Molded
%
520
A
Tensile Elongation?(Break)
Compression Molded
%
520
I
Tensile Strength(Yield)
Compression Molded
MPa
8.34
A
Tensile Strength(Yield)
Compression Molded
MPa
8.34
I
Tensile Elongation
断裂,模压成型
ASTMD638,ISO527-2
%
5
Thermal Properties
Test Condition
Test Method
Unit
EAA/STYRON US/3330
Melting temperature (DSC)
内部方法
°C
1
Vicat Softening Temperature
℃
85
A
Vicat Softening Temperature
℃
85
I
Vicat Softening Temperature
ASTMD1525,ISO306
°C
8
Film
Test Condition
Test Method
Unit
EAA/STYRON US/3330
Peak Melting Temperature
内部方法
°C
9
Water Vapor Transmission Rate
38°C,90%RH
DIN53122/2
g·mm/m²/atm/24hr
0
Processing
Test Condition
Test Method
Unit
EAA/STYRON US/3330
Melt Temperature
℃
260-290
Other
Test Condition
Test Method
Unit
EAA/STYRON US/3330
Sealing Initial Temperature
℃
92.8
I