ABS MG47F-NA1000 SABIC INNOVATIVE MEXICO
CYCOLAC™
--
High impact resistance
UL
FDA
RoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE MEXICO/MG47F-NA1000
Melt Mass-Flow Rate
230°C/3.8 kg
ASTM D1238
g/10 min
5
Melt Mass-Flow Rate
220°C/10.0 kg
ISO 1133
g/10 min
1
Modeling Shrinkage - Flow
3.20 mm
内部方法
%
0
Mechanical Properties
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE MEXICO/MG47F-NA1000
Tensile Strength
屈服 2
ASTM D638
Mpa
4
Tensile Strength
屈服
ISO 527-2/50
Mpa
4
Tensile Strength
断裂 2
ASTM D638
Mpa
3
Tensile Strength
断裂
ISO 527-2/50
Mpa
3
Tensile Modulus
-- 1
ASTM D638
Mpa
2
Tensile Modulus
--
ISO 527-2/1
Mpa
2
Tensile Elongation
屈服 2
ASTM D638
%
2
Tensile Elongation
屈服
ISO 527-2/50
%
2
Tensile Elongation
断裂 2
ASTM D638
%
2
Tensile Elongation
断裂
ISO 527-2/50
%
2
Flexural Modulus
50.0 mm 跨距 3
ASTM D790
Mpa
2
Flexural Modulus
-- 4
ISO 178
Mpa
2
Flexural Stress
-- 4, 5
ISO 178
Mpa
7
Flexural Stress
屈服, 50.0 mm 跨距 3
ASTM D790
Mpa
7
Thermal Properties
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE MEXICO/MG47F-NA1000
RTI
UL 746
°C
6
RTI Elec
UL 746
°C
6
RTI Imp
UL 746
°C
6
Vicat Softening Temperature
--
ISO 306/B50
°C
9
Vicat Softening Temperature
--
ISO 306/B120
°C
1
Linear thermal expansion coefficient
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
8
Linear thermal expansion coefficient
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
8
Deflection Temperature Under Load?
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
9
Deflection Temperature Under Load?
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
8
Deflection Temperature Under Load?
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7
ISO 75-2/Af
°C
8
Fill Analysis
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE MEXICO/MG47F-NA1000
Melt Viscosity
240°C, 1000 sec^-1
ASTM D3835
Pa·s
2
Impact Properties
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE MEXICO/MG47F-NA1000
Charpy Notched Impact Strength
-30°C
ISO 179/1eA
kJ/m²
9
Charpy Notched Impact Strength
23°C
ISO 179/1eA
kJ/m²
2
Instrumented Dart Impact
23°C, Total Energy
ASTM D3763
J
3
Injection
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE MEXICO/MG47F-NA1000
Back Pressure
Mpa
0
Drying Time
hr
2
Drying Temperature
°C
8
Processing (Melt) Temp
°C
2
Suggested Max Moisture
%
0
Suggested Shot Size
%
5
Rear Temperature
°C
1
Front Temperature
°C
2
Middle Temperature
°C
2
Screw Speed
rpm
3
Mold Temperature
°C
5
Vent Depth
mm
0
Nozzle Temperature
°C
2