Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-709S TAIWAN CHIMEI
POLYLAC®
furniture、container
High impact resistance
UL
MSDS
RoHS
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-709S
Density
--3
ASTMD792
g/cm³
1
Density
23°C
ISO1183
g/cm³
1
Melt Volume flow Rate
220°C/10.0kg
ISO1133
cm3/10min
4
Melt Mass-Flow Rate
200°C/5.0kg
ASTMD1238
g/10min
0
Modeling Shrinkage
ISO294-4
%
0
Mechanical Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-709S
Tensile Strength
屈服4
ASTMD638
Mpa
3
Tensile Strength
屈服
ISO527-2/50
Mpa
3
Tensile Strength
断裂
ISO527-2/50
Mpa
2
Tensile Elongation
断裂4
ASTMD638
%
4
Tensile Elongation
断裂
ISO527-2/50
%
3
Flexural Modulus
--5
ASTMD790
Mpa
1
Flexural Modulus
--6
ISO178
Mpa
1
Flexural Strength
--5
ASTMD790
Mpa
5
Flexural Strength
--6
ISO178
Mpa
5
Thermal Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-709S
Deflection Temperature Under Load?
1.8MPa,退火
ASTMD648
°C
9
Deflection Temperature Under Load?
1.8MPa,退火
ISO75-2/A
°C
9
Deflection Temperature Under Load?
1.8MPa,未退火
ASTMD648
°C
8
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/A
°C
8
Vicat Softening Temperature
--
ASTMD15257
°C
1
Vicat Softening Temperature
--
ISO306/A50
°C
1
Vicat Softening Temperature
--
ISO306/B50
°C
9
Linear thermal expansion coefficient
MD
ISO11359-2
cm/cm/°C
9
Impact Properties
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-709S
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
3
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
4
Notched Izod Impact Strength
23°C,3.20mm
ASTMD256
J/m
4
Notched Izod Impact Strength
23°C,6.40mm
ASTMD256
J/m
2
Notched Izod Impact Strength
-30°C
ISO180/1A
kJ/m²
2
Notched Izod Impact Strength
23°C
ISO180/1A
kJ/m²
4