Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PA M/MK 8 A SCHULMAN USA
SCHULABLEND®
--
Filler: Glass fiber reinf、8.0% filler by weight、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Melt Volume flow Rate
250°C/5.0kg
ISO1133
cm3/10min
4
Melt Volume flow Rate
250°C/5.0kg
ISO1133
cm3/10min
2
Mechanical Properties
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Tensile Modulus
ISO527-2/1A/1
Mpa
4
Tensile Modulus
ISO527-2/1A/1
Mpa
3
Tensile Strain
屈服
ISO527-2/1A/50
%
3
Tensile Strain
断裂
ISO527-2/1A/5
%
4
Tensile Stress
屈服
ISO527-2/1A/50
Mpa
4
Tensile Stress
断裂
ISO527-2/1A/5
Mpa
7
Thermal Properties
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Deflection Temperature Under Load?
0.45MPa,未退火
ISO75-2/Bf
°C
1
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/Af
°C
1
Deflection Temperature Under Load?
0.45MPa,未退火
ISO75-2/Bf
°C
1
Deflection Temperature Under Load?
1.8MPa,未退火
ISO75-2/Af
°C
7
Vicat Softening Temperature
--
ISO306/A50
°C
1
Vicat Softening Temperature
--
ISO306/B50
°C
1
Vicat Softening Temperature
--
ISO306/A50
°C
2
Vicat Softening Temperature
--
ISO306/B50
°C
1
Electrical performance
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Surface Resistivity
IEC60093
ohms
>
Volume Resistivity
IEC60093
ohms·cm
>
Impact Properties
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Charpy Unnotched Impact Strength
23°C
ISO179/1eU
kJ/m²
7
Charpy Unnotched Impact Strength
23°C
ISO179/1eU
kJ/m²
3
hardness
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Ball Indentation Hardness
H358/30
ISO2039-1
Mpa
9
Ball Indentation Hardness
H358/30
ISO2039-1
Mpa
9
Flammability
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Burning Rate
ISO3795
mm/min
<