Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 1000 GY SABIC INNOVATIVE US
ULTEM™
Electrical field、Electronic field、Automotive sector
Glass fiber reinforced、Flame retardant、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Melt Volume flow Rate
360°C/5.0 kg
ISO 1133
cm3/10min
1
Modeling Shrinkage - Flow
内部方法
%
0
Moisture Absorption
饱和, 23°C
ISO 62
%
1
Moisture Absorption
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Tensile Modulus
ISO 527-2/1
Mpa
3
Tensile Strain
屈服
ISO 527-2/50
%
6
Tensile Strain
断裂
ISO 527-2/50
%
6
Tensile Stress
屈服
ISO 527-2/50
Mpa
1
Tensile Stress
断裂
ISO 527-2/50
Mpa
8
Taber Abrasion Resistance
1000 Cycles, 1000 g, CS-17 转轮
内部方法
mg
1
Flexural Modulus
ISO 178
Mpa
3
Flexural Stress
ISO 178
Mpa
1
Thermal Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Thermal Conductivity
ISO 8302
W/m/K
0
Heat Deflection Temperature
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距
ISO 75-2/Be
°C
2
Heat Deflection Temperature
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距
ISO 75-2/Ae
°C
1
Vicat Softening Temperature
--
ISO 306/A50
°C
2
Vicat Softening Temperature
--
ISO 306/B50
°C
2
Vicat Softening Temperature
--
ISO 306/B120
°C
2
Linear thermal expansion coefficient
流动 : 23 到 150°C
ISO 11359-2
cm/cm/°C
5
Linear thermal expansion coefficient
横向 : 23 到 150°C
ISO 11359-2
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Surface Resistivity
IEC 60093
ohms
>
Dielectric Strength
0.800 mm, 在油中
IEC 60243-1
KV/mm
3
Dielectric Strength
1.60 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric Strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Comparative Tracking Index
--
IEC 60112
V
1
Comparative Tracking Index
解决方案 B
IEC 60112
V
1
Volume Resistivity
IEC 60093
ohms·cm
1
Impact Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Notched Izod Impact Strength
-30°C
ISO 180/1A
kJ/m²
6
Notched Izod Impact Strength
23°C
ISO 180/1A
kJ/m²
6
hardness
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Ball Indentation Hardness
H 358/30
ISO 2039-1
Mpa
1
Flammability
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Oxygen Index
ISO 4589-2
%
4
Glow Wire Flammability Index
3.2 mm
IEC 60695-2-12
°C
9
Injection
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/1000 GY
Drying Time
hr
4
Drying Temperature
°C
1
Processing (Melt) Temp
°C
3
Suggested Max Moisture
%
0
Hopper Temperature
°C
8
Rear Temperature
°C
3
Front Temperature
°C
3
Middle Temperature
°C
3
Mold Temperature
°C
1
Nozzle Temperature
°C
3