Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E6810LHF-BZ SUMITOMO JAPAN
SUMIKASUPER®
--
Low warpage、Good forming performance、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
Modeling Shrinkage
流动
ASTM D955
%
0
Modeling Shrinkage
横向流动
ASTM D955
%
0
Moisture Absorption
饱和
ASTM D570
%
0
Mechanical Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
Shearing Strength
ASTM D732
Mpa
5
Tensile Strength
ASTM D638
Mpa
1
Tensile Elongation
断裂
ASTM D638
%
4
Flexural Modulus
23°C
ASTM D790
Mpa
1
Flexural Strength
23°C
ASTM D790
Mpa
1
Thermal Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
RTI
3.2 mm
UL 746
°C
2
RTI Elec
3.2 mm
UL 746
°C
2
RTI Imp
3.2 mm
UL 746
°C
2
Linear thermal expansion coefficient
流动 : 50 到 150°C
ASTM D696
cm/cm/°C
1
Linear thermal expansion coefficient
横向 : 50 到 150°C
ASTM D696
cm/cm/°C
6
Deflection Temperature Under Load?
1.8 MPa, 未退火
ASTM D648
°C
2
Electrical performance
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
Arc Resistance
ASTM D495
sec
1
Volume Resistivity
ASTM D257
ohms·cm
1
Comparative Tracking Index
UL 746
V
1
Impact Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
Unnotched Izod Impact Strength
6.40 mm
ASTM D256
J/m
2
Flammability
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
Oxygen Index
ASTM D2863
%
4
Injection
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6810LHF-BZ
Holding Pressure
Mpa
2
Back Pressure
Mpa
0
Drying Time
hr
3
Drying Temperature
°C
1
Suggested Max Regrind
%
3
Rear Temperature
°C
3
Front Temperature
°C
3
Middle Temperature
°C
3
Screw Speed
rpm
5
Mold Temperature
°C
7
Nozzle Temperature
°C
3
Injection Pressure
Mpa
7