Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 2210EPR SABIC INNOVATIVE US
ULTEM™
Automotive components、Lighting fixtures
Thermal stability、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR
Melt Mass-Flow Rate
337°C/6.6kg
ASTMD1238
g/10min
1
Modeling Shrinkage
MD：3.20mm
内部方法
%
0
Modeling Shrinkage
TD：3.20mm
内部方法
%
0
Mechanical Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR
Flexural Strength
Break,100mmSpan
ASTMD790
Mpa
2
Flexural Strength
Yield,50.0mmSpan
ASTMD790
Mpa
2
Tensile Strength
屈服
ASTMD638
Mpa
1
Tensile Strength
断裂
ASTMD638
Mpa
1
Tensile Modulus
ASTMD638
Mpa
6
Tensile Elongation
屈服
ASTMD638
%
3
Tensile Elongation
断裂
ASTMD638
%
3
Flexural Modulus
100mmSpan4
ASTMD790
Mpa
6
Flexural Modulus
50.0mm跨距5
ASTMD790
Mpa
6
Thermal Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
Deflection Temperature Under Load?
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Deflection Temperature Under Load?
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Deflection Temperature Under Load?
1.8MPa,未退火,6.40mm
ASTMD648
°C
2
Deflection Temperature Under Load?
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Vicat Softening Temperature
ASTMD15256
°C
2
Linear thermal expansion coefficient
MD：-40到40°C
ASTME831
cm/cm/°C
3
Linear thermal expansion coefficient
TD：-40到40°C
ASTME831
cm/cm/°C
7
Impact Properties
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR
Instrumented Dart Impact
23°C,TotalEnergy
ASTMD3763
J
1