Melt Viscosity

250°C,1500sec^-1

ISO11443

Pa·s

2

Melt Volume flow Rate

250°C/5.0kg

ISO1133

cm3/10min

2

Melt Mass-Flow Rate

250°C/5.0kg

ASTMD1238

g/10min

2

Modeling Shrinkage

MD：--2

内部方法

%

0

Modeling Shrinkage

MD：3.20mm

内部方法

%

0

Modeling Shrinkage

TD：--2

内部方法

%

0

Modeling Shrinkage

TD：3.20mm

内部方法

%

0

Moisture Absorption

饱和,23°C

ISO62

%

0

Moisture Absorption

平衡,23°C,50%RH

ISO62

%

0

Flexural Strength

Yield,50.0mmSpan

ASTMD790

Mpa

1

Flexural Strain (Break)

ISO178

%

2

Tensile Strength

屈服

ASTMD638

Mpa

1

Tensile Modulus

ISO527-2/1

Mpa

1

Tensile Modulus

ASTMD638

Mpa

9

Tensile Strength

Break

ASTMD638

Mpa

1

Tensile Strain

断裂

ISO527-2/5

%

2

Tensile Strain

屈服

ISO527-2/5

%

2

Tensile Stress

断裂

ISO527-2/5

Mpa

1

Tensile Stress

屈服

ISO527-2/5

Mpa

1

Tensile Elongation

屈服

ASTMD638

%

2

Tensile Elongation

断裂

ASTMD638

%

2

Flexural Modulus

50.0mmSpan

ASTMD790

Mpa

9

Flexural Modulus

ISO178

Mpa

9

Flexural Strength

ISO178

Mpa

1

RTIElec

UL746

°C

1

Evolution Calendar intelligent importer

UL746

°C

1

RTIStr

UL746

°C

1

Deflection Temperature Under Load?

0.45MPa,未退火,3.20mm

ASTMD648

°C

2

Deflection Temperature Under Load?

1.8MPa,未退火,3.20mm

ASTMD648

°C

2

Heat Deflection Temperature

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

2

Heat Deflection Temperature

0.45MPa,Unannealed,64.0mmSpan

ISO75-2/Bf

°C

2

Vicat Softening Temperature

--

ASTMD152512

°C

2

Vicat Softening Temperature

--

ASTMD152513

°C

2

Vicat Softening Temperature

--

ISO306/A50

°C

2

Vicat Softening Temperature

--

ISO306/B50

°C

2

Vicat Softening Temperature

--

ISO306/B120

°C

2

Linear thermal expansion coefficient

MD：-40to40°C

ASTME831

cm/cm/°C

2

Linear thermal expansion coefficient

MD：-40to150°C

ASTME831

cm/cm/°C

2

Linear thermal expansion coefficient

MD：-40to40°C

ISO11359-2

cm/cm/°C

3

Linear thermal expansion coefficient

MD：23到80°C

ISO11359-2

cm/cm/°C

2

Linear thermal expansion coefficient

TD：-40to40°C

ASTME831

cm/cm/°C

7

Linear thermal expansion coefficient

TD：-40to150°C

ASTME831

cm/cm/°C

7

Linear thermal expansion coefficient

TD：-40to40°C

ISO11359-2

cm/cm/°C

7

Linear thermal expansion coefficient

TD：23到80°C

ISO11359-2

cm/cm/°C

9

Dielectric Strength

3.20mm,在油中

ASTMD149

KV/mm

2

Dielectric Strength

3.20mm,inAir

ASTMD149

KV/mm

2

Comparative Tracking Index

IEC60112

V

3

Volume Resistivity

ASTMD257

ohms·cm

1

Volume Resistivity

IEC60093

ohms·cm

1

Charpy Unnotched Impact Strength

-30°C

ISO179/2U

kJ/m²

3

Charpy Unnotched Impact Strength

23°C

ISO179/2U

kJ/m²

3

Unnotched Izod Impact Strength

-30°C

ISO180/1U

kJ/m²

2

Unnotched Izod Impact Strength

23°C

ISO180/1U

kJ/m²

3

Notched Izod Impact Strength

23°C

ISO180/1A

kJ/m²

7

Notched Izod Impact Strength

-30°C

ISO180/1A

kJ/m²

7

Instrumented Dart Impact

23°C,TotalEnergy

ASTMD3763

J

6

Glow Wire Ignition Temperature

0.8mm

IEC60695-2-13

°C

7

Glow Wire Ignition Temperature

3.0mm15

IEC60695-2-13

°C

7

Glow Wire Flammability Index

0.75mm

IEC60695-2-12

°C

9