Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTMD955 | 0.17到0.20 | % |
| Water absorption rate | 23°C,24hr | ASTMD570 | <0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus | | ASTMD790 | 10800到11800 | Mpa |
| bending strength | | ASTMD790 | 118到127 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 275 | °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | --2 | ASTMD257 | 1.0E+13到1.0E+14 | ohms·cm |
| Volume resistivity | --3 | ASTMD257 | 1.0E+12到1.0E+13 | ohms·cm |
| Dielectric strength | | ASTMD149 | 27到30 | KV/mm |
| Arc resistance | | ASTMD495 | 190 | sec |
| Compared to the anti leakage trace index | CTI | UL746 | >600 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.