Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTMD955 | 0.40 | % |
| Shrinkage rate | TD | ASTMD955 | 0.80 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.23 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 断裂,23°C | ISO527-2 | 210 | Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 2.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 12000 | Mpa |
| Bending modulus | 23°C | ISO178 | 10700 | Mpa |
| Bending stress | 23°C | ISO178 | 295 | Mpa |
| Bending strain | | ISO178 | 3.1 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass transition temperature | | DSC | 95.0 | °C |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.5E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：0to100°C | ASTME831 | 7.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 327 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | >300 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric constant | 60Hz | ASTMD150 | 4.10 | |
| Dielectric constant | 1MHz | ASTMD150 | 3.75 | |
| Volume resistivity | | ASTMD257 | 5.6E+15 | ohms·cm |
| Dielectric strength | 3.20mm | ASTMD149 | 19 | KV/mm |
| Dissipation factor | 1MHz | ASTMD150 | 0.015 | |
| Dissipation factor | 60Hz | ASTMD150 | 6E-03 | |
| High voltage arc tracing rate | HVTR | UL746 | 14.0 | mm/min |
| Compared to the anti leakage trace index | CTI | UL746 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO180/1U | 68 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 79 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating2 | 3.2mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.