Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 190℃/2.16kg | ASTM D-1238 | 5 | g/10min |
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 5.0 | g/10min |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 5.0 | g/10min |
| GlycidylMethacrylateContent | | | 8.0 | wt% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength at break | | ASTM D-638 | 8 | Mpa |
| hardness | D | ASTM D-2240 | 50 | |
| Tensile stress | 断裂,模压成型 | ISO527-2 | 8.00 | Mpa |
| Tensile strain | 断裂,模压成型 | ISO527-2 | 400 | % |
| Tensile modulus | | ASTM D-638 | 104 | Mpa |
| elongation | 断裂 | ASTM D-638 | 400 | % |
| elongation | 断裂,模压成型 | ASTMD638 | 400 | % |
| Bending modulus | 模压成型 | ASTMD790 | 85.0 | Mpa |
| Bending modulus | 模压成型 | ISO178 | 85.0 | Mpa |
| Bending modulus | | ASTM D-790 | 85 | Mpa |
| Tensile strength | 断裂,模压成型 | ASTMD638 | 8.00 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTM D-1525 | 87 | °C |
| Vicat softening temperature | | ASTMD15252 | 87.0 | °C |
| Vicat softening temperature | | ISO306/A | 87.0 | °C |
| Melting temperature | | DSC | 106 | °C |
| Melting temperature | | ISO11357-3 | 106 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D,1秒,模压成型 | ISO868 | 50 | |
| DurometerHardness | ShoreD,1sec,CompressionMolded | ASTMD2240 | 50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.