Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| MeltViscosity3 | 260°C | ISO11443-A | 160 | Pa·s |
| Melt volume flow rate | 240°C/5.0kg | ISO1133 | 24.0 | cm3/10min |
| Shrinkage rate 2 | TD:240°C,3.00mm | ISO2577 | 0.50to0.70 | % |
| Shrinkage rate 2 | MD:240°C,3.00mm | ISO2577 | 0.50to0.70 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.50 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
| Density/specific gravity | 23°C | ISO1183 | 1.18 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2700 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 60.0 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2/50 | 45.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 3.5 | % |
| Tensile strain | 断裂,23°C | ISO527-2/50 | >40 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 92.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 82.0 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 95.0 | °C |
| Vicat softening temperature | -- | ISO306/B120 | 97.0 | °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 7.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+16 | ohms |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
| Relative permittivity | 23°C,1MHz | IEC60250 | 3.10 | |
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-03 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 6E-03 | |
| Leakage Trace Index | 解决方案A | IEC60112 | 350 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 35 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180 | NoBreak | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| UL flame retardant rating | 2.0mm | UL94 | 5VB | |
| UL flame retardant rating | 3.0mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.