Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.23 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 2.8 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 3.0 | g/10min |
| Apparent density | | ISO60 | 1.05 | g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.40到0.70 | % |
| density | | ASTMD792 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 屈服 | ISO527-2/50 | 46.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 35.0 | Mpa |
| Tensile stress | 3.00mm3 | ASTMD638 | 47.1 | Mpa |
| elongation | 断裂,3.00mm3 | ASTMD638 | 50 | % |
| elongation | 断裂 | ISO527-2/50 | 25 | % |
| Bending modulus | 6.00mm4 | ASTMD790 | 2350 | Mpa |
| Bending modulus | --5 | ISO178 | 1800 | Mpa |
| bending strength | 6.00mm4 | ASTMD790 | 68.6 | Mpa |
| bending strength | --5 | ISO178 | 63.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 85.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 84.0 | °C |
| Hot deformation temperature | 1.8MPa,退火 | ASTMD648 | 95.0 | °C |
| Hot deformation temperature | 1.8MPa,退火 | ISO75-2/A | 100 | °C |
| Vicat softening temperature | -- | ASTMD15256,ISO306/A506 | 106 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 101 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.7E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 24 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 35 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.00mm | ASTMD256 | 440 | J/m |
| Impact strength of cantilever beam gap | 23°C,6.00mm | ASTMD256 | 310 | J/m |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 22 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 33 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.