Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ISO294-4 | 0.50到0.90 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.60 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.16 | % |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 18.0 | cm3/10min |
| Density/specific gravity | | ISO1183 | 1.16 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress | | ISO178 | 93.0 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 62.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 4.9 | % |
| Tensile modulus | | ISO527-2 | 2500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7.0E-5到9.0E-5 | cm/cm/°C |
| Vicat softening temperature | -- | ISO306/A50 | 140 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 130 | °C |
| thermal conductivity | | DIN52612 | 0.17 | W/m/K |
| Hot deformation temperature 2 | 0.45MPa,退火 | ISO75-2/B | 130 | °C |
| Hot deformation temperature 2 | 1.8MPa,退火 | ISO75-2/A | 109 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+14 | ohms |
| Dielectric constant | 100Hz | IEC60250 | 3.10 | |
| Volume resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Dissipation factor | 100Hz | IEC60250 | 6E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 0.010 | |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation MD | 断裂 | ISO527-3 | >50 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 17 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 60 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 110 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.