Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | 23°C | ISO527-2 | 28 | Mpa |
| elongation at break | 23°C | ISO527-2 | 50 | % |
| bending strength | 23°C | ISO178 | 45 | Mpa |
| Bending modulus | 23°C | ISO178 | 1400 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 10 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 100 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 9.00 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.80MPa退火 | ISO75-2/A | 95 | °C |
| Hot deformation temperature | 1.80MPa退火 | ISO75-2/Af | 79 | °C |
| Vicat softening temperature | | ISO306/A50 | 100 | °C |
| Vicat softening temperature | | ISO306/B50 | 91 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 93 | Mpa |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | | UL-94 | 1.50mm | HB |
| Fire rating | | UL-94 | 3.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.