PET Rynite® 530 NC010 DUPONT USA

424

Properties:
enhance
Glass fiber reinforced
wear resistant
High rigidity
High temperature resistan
Filler: Glass fiber reinf
30% filler by weight
Usages:
Electrical field
Electronic field
Household appliances
Household appliances
Automotive sector
Certificates:
UL
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	饱和,23°C,2.00mm	ISO62	0.75	%
Water absorption rate	Water absorption rate	平衡,23°C,2.00mm,50%RH	ISO62	0.15	%
Shrinkage rate	TD	ISO294-4	0.80	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.20	%
Melt volume flow rate	280°C/2.16kg	ISO1133	6.00	cm3/10min
Top out temperature			170	°C
Density/specific gravity		ISO1183	1.68	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
TensileCreepModule	1hr	ISO899-1	11200	Mpa
Tensile creep modulus	1000hr	ISO899-1	9700	Mpa
Tensile stress	断裂	ISO527-2	135	Mpa
Tensile strain	断裂	ISO527-2	2.0	%
Tensile modulus		ISO527-2	11500	Mpa
Bending modulus		ISO178	10500	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,未退火	ISO75-2/B	243	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	225	°C
RTIElec	0.40mm	UL746	155	°C
	RTIElec	0.75mm	UL746	155	°C
		RTIElec	1.5mm	UL746	155	°C
		RTIElec	RTIElec	3.0mm	UL746	155	°C
Evolution Calendar intelligent importer	0.40mm	UL746	155	°C
	Evolution Calendar intelligent importer	0.75mm	UL746	155	°C
		Evolution Calendar intelligent importer	1.5mm	UL746	155	°C
		Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	155	°C
RTIStr	0.40mm	UL746	155	°C
	RTIStr	0.75mm	UL746	155	°C
		RTIStr	1.5mm	UL746	155	°C
			RTIStr	3.0mm	UL746	155	°C
			RTIStr	RTIStr	EffectiveThermalDiffusivity	UL746	1.1E-07	m²/s
Vicat softening temperature		ISO306/B50	220	°C
Melting temperature 2		ISO11357-3	252	°C
Linear coefficient of thermal expansion	MD：-40to23°C	ISO11359-2	2.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：--	ISO11359-2	9.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to23°C	ISO11359-2	6.8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO11359-2	1.9E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		IEC60243-1	39	KV/mm
Compared to the anti leakage trace index	CTI	UL746	PLC2
Dissipation factor	100Hz	IEC60250	7E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.013
Surface resistivity		IEC60093	1E+14	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Relative permittivity	100Hz	IEC60250	4.80
Relative permittivity	Relative permittivity	1MHz	IEC60250	4.30
Leakage Trace Index		IEC60112	200	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	10	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	40	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	40	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.35mm	UL94	V-0
	UL flame retardant rating	1.5mm	UL94	V-05VA
		UL flame retardant rating	0.35mm	IEC60695-11-10,-20	V-0
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	V-05VA
Extreme Oxygen Index		ISO4589-2	33	%
FMVSS flammability		FMVSS302	DNI

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PET Rynite® 530 NC010 DUPONT USA

Technical Data Sheet