Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 横向流量 | 内部方法 | 0.30 到 0.70 | % |
| Shrinkage rate | 流量 | 内部方法 | 0.10 到 0.40 | % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.020 | % |
| density | | ISO 1183 | 1.45 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress | | ISO 178 | 170 | Mpa |
| Tensile stress | 断裂 | ISO 527-2 | 110 | Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 | % |
| Tensile modulus | | ISO 527-2 | 10500 | Mpa |
| Bending modulus | | ISO 178 | 10300 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 265 | °C |
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 230 | °C |
| RTI | | UL 746 | 130 | °C |
| RTI Imp | | UL 746 | 120 | °C |
| RTI Elec | | UL 746 | 130 | °C |
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | TMA | 1.9E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : -30 到 30°C | TMA | 4.2E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | ASTM D149 | 35 | KV/mm |
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | 1.5 mm | UL 746 | PLC 2 | |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) of 4 | | IEC 60112 | PLC 1 | |
| Dissipation factor | 1 MHz | IEC 60250 | 2.0E-3 | |
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 | |
| High arc combustion index (HAI) | 1.5 mm | UL 746 | PLC 0 | |
| Dielectric constant | 1 MHz | IEC 60250 | 3.00 | |
| Arc resistance | | ASTM D495 | PLC 6 | |
| Volume resistivity | | IEC 60093 | > 1.0E+16 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 120 | °C |
| Processing (melt) temperature | | | 280 到 310 | °C |
| Mold temperature | | | 130 到 155 | °C |
| drying time | | | 3.0 到 5.0 | hr |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 28 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 8.0 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO 180 | 26 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | > 0.75 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.