ABS POLYLAC®  PA-797 TAIWAN CHIMEI

674
  • Properties:
    High gloss
  • Usages:
    Electrical field
    Electronic field
  • Certificates:
    UL

Technical Data Sheet

Physical propertiesTest ConditionTest MethodTest ResultUnit
Melt index (flow coefficient)ASTM D1238/ISO 11331g/10min
densityASTM D792/ISO 11831.05
physical property Test ConditionTest MethodTest ResultUnit
Melt index200℃*5kgASTM D12380.8g/10min
Melt index200℃*10kgISO 113310.0g/10min
Mechanical performanceTest ConditionTest MethodTest ResultUnit
Rockwell hardnessASTM D785R-108R scale
Tensile strength降伏点ASTM D638440kg/cm2
Elongation rateASTM D63850%
bending strength ASTM D790610kg/cm2
Flexural elasticityASTM D79020500kg/cm2
tensile strength ASTM D638/ISO 527420kg/cm²(MPa)[Lb/in²]
Rockwell hardnessASTM D785108
Bending modulusASTM D790/ISO 17820500kg/cm²(MPa)[Lb/in²]
bending strength ASTM D790/ISO 178610kg/cm²(MPa)[Lb/in²]
IZOD impact strength1/4"切口ASTM D25631Kg/cm.cm
IZOD impact strength1/8"切口ASTM D25644Kg/cm.cm
IZOD notch impact strengthASTM D256/ISO 17927kg·cm/cm(J/M)ft·lb/in
IZOD notch impact strengthASTM D256/ISO 17940kg·cm/cm(J/M)ft·lb/in
Thermal performanceTest ConditionTest MethodTest ResultUnit
softening pointASTM D1525106.0°C
Hot deformation temperatureASTM D64886.0°C
Combustibility (rate)UL941/16
Hot deformation temperatureASTM D648/ISO 7597℃(℉)
Hot deformation temperatureASTM D648/ISO 7586℃(℉)
vicat softening point ASTM D1525/ISO R306105.5℃(℉)
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.