Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 190°C/2.16 kg | ASTM D1238, ISO 1133 | 35 | g/10 min |
| molecular weight distribution | | ASTM D3593 | Normal | |
| Hardness tester hardness | 支撐 A | ASTM D2240 | 55 | |
| Melt flow index | 190℃/2.16Kg | ASTMD1238 | 35.00 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | | ASTM D638 | 4.20 | Mpa |
| elongation | 断裂 | ASTM D638 | 1200 | % |
| tensile strength | 23°C | ASTMD638 | 4.20 | Mpa |
| elongation at break | 23°C | ASTMD638 | 1200 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | 玻璃转化温度 | ASTMD648 | -32 | °C |
| Vicat softening temperature | 熔融温度 | ASTMD4591 | 45 | °C |
| Glass transition temperature | | ASTM D1525, ISO 306 | -32.2 | °C |
| Melting temperature | | ASTM D3418, ISO 3146 | 45.0 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shaw Brothers A | | ASTMD2240 | 55 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.