ABS TAIRILAC® AG10AP FCFC TAIWAN
1564
- Properties:High rigidityHigh impact resistanceUsed for extrusion moldiUltra high impact resistaHigh rigidity
- Usages:ABS pipeHelmetHelmet
- Certificates:ULMSDSTDSProcessingMSDSULRoHSSVHCEnvironmental
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.04 | g/cm³ | |
| 23°C | ISO1183 | 1.04 | g/cm³ | |
| 220°C/10.0kg | ASTMD1238 | 4.5 | g/10min | |
| 220°C/10.0kg | ISO1133 | 4.5 | g/10min | |
| Shrinkage rate | MD | 内部方法 | 0.40to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | 23°C | ASTMD638 | 34.3 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 34.0 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 1960 | Mpa |
| 23°C | ISO178 | 1960 | Mpa | |
| bending strength | 23°C | ASTMD790 | 57.0 | Mpa |
| Bending stress | 23°C | ISO178 | 57.0 | Mpa |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 410 | J/m |
| 23°C,6.35mm | ASTMD256 | 410 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 84.0 | °C |
| Vicat softening temperature | ASTMD15253 | 100 | °C | |
| ISO306/A | 100 | °C | ||
| Hot deformation temperature | 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 84.0 | °C |
| 1.8MPa,Annealed | ASTMD648 | 94.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 94.0 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.