Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ASTM D-955 | 0.3-0.6 | % |
| Density/specific gravity | | ASTM D-792 | 1.04 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| IZOD notch impact strength | 3.2mm,Notched(1/8in) | ASTM D-256 | 1.5(0.27) | kg.cm/cm(ft.ld/in) |
| tensile strength | 23℃ | ASTM D-638 | 540(7670) | kg/cm2(psi) |
| elongation | | ASTM D-638 | 3.5 | % |
| Rockwell hardness | | ASTM D-785 | 75 | M Scale |
| Bending modulus | 23℃ | ASTM D-790 | 33000(454400) | kg/cm2(psi) |
| bending strength | 23℃ | ASTM D-790 | 890(12640) | kg/cm2(psi) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 6.4mm,18.6kg/cm2(1/4in 264Psi)Unannealed | ASTM D-648 | 87(189) | ℃（℉） |
| vicat softening point | | ASTM D-1525 | 105(221) | ℃（℉） |
| Flame retardancy | 1/16"(1.6mm) | UL 94 | HB | |
| Flame retardancy | 1/12"(2.2mm) | UL 94 | HB | |
| Flame retardancy | 1/8"(3.2mm) | UL 94 | HB | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Voltage endurance | | ASTM D-149 | 550 | v/mil |
| Volume resistivity | | ASTM D-257 | 1016 | Ω.cm |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃,5kg | ASTM D-1238 | 3.0 | g/10min |
| Water absorption rate | | ASTM D-570 | 0.03 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.