Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| Shrinkage rate | MD：3.20mm | ISO294-4 | 0.40to0.70 | % |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 6.0 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 6.0 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.08 | g/cm³ |
| Density/specific gravity | | ISO1183 | 1.08 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus 4 | | ISO178 | 2400 | Mpa |
| FlexuralStrength3 | 6.40mm | ASTMD790 | 75.5 | Mpa |
| Bending modulus 3 | 6.40mm | ASTMD790 | 2300 | Mpa |
| Tensile strength 2 | 屈服,3.20mm | ASTMD638 | 47.1 | Mpa |
| Elongation rate 2 | 断裂,3.20mm | ASTMD638 | 20 | % |
| Bending stress 4 | | ISO178 | 75.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 48.0 | Mpa |
| Tensile modulus | | ISO527-2/1 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 94.0 | °C |
| Vicat softening temperature | | ASTMD15256 | 102 | °C |
| Vicat softening temperature | | ISO306/B50 | 102 | °C |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| Hot deformation temperature 5 | 1.8MPa,Unannealed,4.00mm | ISO75-2/Ae | 88.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 11 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTMD256 | 140 | J/m |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 12 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ASTMD785 | 104 | |
| Rockwell hardness | | ISO2039-2 | 104 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.