Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 260°C/5.0kg | ASTMD1238 | 9.0 | g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.10 | % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus 2 | | ASTMD638 | 2210 | Mpa |
| Tensile strength 3 | 屈服 | ASTMD638 | 56.5 | Mpa |
| Elongation rate 3 | 屈服 | ASTMD638 | 5.0 | % |
| Elongation rate 4 | 断裂 | ASTMD638 | 150 | % |
| Bending modulus 4 | 50.0mm跨距 | ASTMD790 | 2340 | Mpa |
| Bending strength 4 | 屈服,50.0mm跨距 | ASTMD790 | 86.2 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 124 | °C |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 107 | °C |
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 110 | °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.20 | W/m/K |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 54.2 | J |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 61.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices